» home » heat shrink » 2:1, 3:1, 4:1 heat shrink tubing » 2:1 heat shrink tubing specifications
|
Back to 2:1 Heat Shrink
| 3/64" |
0.055 |
1.4 |
0.022 |
0.58 |
0.013 |
0.330 |
| 1/16" |
0.075 |
1.9 |
0.031 |
0.79 |
0.014 |
0.356 |
| 3/32" |
0.110 |
2.8 |
0.046 |
1.17 |
0.017 |
0.432 |
| 1/8" |
0.138 |
3.5 |
0.062 |
1.57 |
0.017 |
0.432 |
| 3/16" |
0.200 |
5.0 |
0.093 |
2.36 |
0.017 |
0.432 |
| 1/4" |
0.256 |
6.5 |
0.125 |
3.18 |
0.022 |
0.559 |
| 3/8" |
0.380 |
9.6 |
0.187 |
4.75 |
0.022 |
0.559 |
| 1/2" |
0.500 |
12.8 |
0.250 |
6.35 |
0.022 |
0.559 |
| 3/4" |
0.760 |
19.3 |
0.370 |
9.35 |
0.027 |
0.686 |
| 1" |
1.02 |
25.7 |
0.500 |
12.7 |
0.030 |
0.762 |
| 1-1/4" |
1.26 |
32.2 |
0.630 |
16.0 |
0.034 |
0.864 |
| 1-1/2" |
1.5 |
38.1 |
0.586 |
14.9 |
0.034 |
0.864 |
| 2" |
2.0 |
51.0 |
1.0 |
25.4 |
0.038 |
0.965 |
| 3" |
3.0 |
76.2 |
1.5 |
38.1 |
0.042 |
1.07 |
| 4" |
4.0 |
102.0 |
2.0 |
50.8 |
0.046 |
1.17 |
| 5" |
5.0 |
127.0 |
2.5 |
63.5 |
0.046 |
1.17 |
| |
|
Tensile Strength |
ASTM D 638 |
13 N/mm² |
Elongation at Break |
ASTM D 638 |
400% |
Longitudinal Change |
ASTM D 2671 |
+5%,-5% maximum |
Water Absorption |
ASTM D 570 |
0.15% Maximum |
Specific Gravity |
ASTM D 792 |
1.4 |
| |
|
Dielectric Strength |
ASTM D 2671 |
25kV/mm |
Volume Resistivity |
ASTM D 257 |
10@ 14 ohm.cm |
| |
|
Fungus Resistance |
MIL-I-7444 |
Inert |
Fluid Resistance |
MIL-I-23053/5 |
Good |
Cooper Corrosion |
ASTM D 2671 B |
Good |
| |
|
Continuous Operating Temperature |
|
-55°C to +135VC |
Minimum Shrink Temperature |
|
>90°C |
Heat Shock 4 hours at 250°C |
ASTM D 2671 |
No dripping, cracking or flowing |
Heat Aging 168 hours at 150°C |
ASTM D 638 |
Elongation 300% |
Low Temperature Flexibility -55°C |
ASTM D 2671C |
No cracking |
Flammability |
UL 224VWI |
Pass (colors only) |
*Clear Tubing is not Flame Retarded
Specification reference:
UL 224 125°C, 600V, VW-1
CSA-C22.2 No. 198-M1986 125°C, 600V
File LR33298 Guide 400-U-9
Back to 2:1 Heat Shrink
Features:
- Shrink ratio: 50% or more in the radial direction
- Operating temperature: -55°C to 125°C
- Flammability: Ul VW-1 (Jacket only)
- Minimum shrink temperature: 90°C
|
Standard:
- MIL-DTL-23053/4 Class2
- UL 224 (File Number: E153276)
- CSA C22.2 (Reference Standard)
|
| Physical |
Unaged |
Tensile strength |
ASTM D 638
UL 224 |
Min. 1.1kgf/mm² |
| Elongation |
Min. 200% |
Aged |
Tensile strength |
ASTM D 638
UL 224
175°C/168hrs |
Min. 0.8kgf/mm² |
| Elongation |
Min. 100% |
Density |
ASTM D-792 |
Max. 1.40g/cm²@23°C |
Heat Shock |
MIL-I-23053 |
Pass @ 250°Cx4hrs |
Low Temperature Flex |
MIL-I-23053 |
No crack @ -55°C |
Flexibility |
158°C/168 hrs |
No crack |
Secant Modulus |
UL 224 |
Max. 173MPa |
| |
| Electrical |
Dielectric Strength |
UL 224 |
Min. 2500V |
Volume resistivity |
UL 224 |
Min. 1x1014Ω - cm |
| |
| Chemical |
Copper Corrosion |
MIL-I-23053
175°C/16hrs |
No Corrision |
Copper Stability
Elongation |
UL 224
158C/16hrs |
UL 224
158C/16hrs |
No sign of degradation
MIn. 100% |
Flammability (vW-1) |
UL 224 |
UL 224 |
Pass |
| 1/8” |
0.126 |
3.2 |
.062 |
1.57 |
0.025 |
0.43 |
0.008 |
0.20 |
4 |
| 3/16” |
0.189 |
4.8 |
.093 |
2.36 |
0.025 |
0.43 |
0.008 |
0.20 |
4 |
| 1/4” |
0.252 |
6.4 |
.125 |
3.18 |
0.030 |
0.56 |
0.008 |
0.20 |
4 |
| 3/8” |
0.378 |
9.6 |
.187 |
4.75 |
0.030 |
0.56 |
0.012 |
0.30 |
4 |
| 1/2” |
0.500 |
12.7 |
.250 |
6.35 |
0.030 |
0.56 |
0.012 |
0.30 |
4 |
| 3/4” |
0.752 |
19.1 |
.375 |
9.53 |
0.035 |
0.69 |
0.012 |
0.30 |
4 |
| 1” |
1.00 |
25.4 |
.50 |
12.70 |
0.040 |
0.76 |
0.012 |
0.30 |
4 |
| 1-1/2” |
1.50 |
38.1 |
.75 |
19.10 |
0.043 |
0.86 |
0.012 |
0.30 |
4 |
|
|